Reduction Of Environmental Pressure By Giving Cementing Material Properties To The Ferrous Slags
Abstract
There are two main kinds of slag in modern steelmaking industry: the electric arc furnace slag (the EAF slag) which is produced in the manufacture of crude steel by the electric arc furnace process and the ladle furnace basic slag (the LF slag) which is produced at the final stages of steelmaking, when the steel is desulfurized in the transport ladle, during what is generally known as the secondary metallurgy process.
Keywords: ladle furnace slag, EAF slag, pig iron, cement clinker, chemical composition, phase composition
References
[1] Z. Huaiwei and H. Xin, “An overview for the utilization of wastes from stainless steel industries,” Resources, Conservation and Recycling, vol. 55, no. 8, pp. 745–754, 2011.
[2] C. Pellegrino, P. Cavagnis, F. Faleschini, and K. Brunelli, “Properties of concretes with black/oxidizing electric arc furnace slag aggregate,” Cement and Concrete Composites, vol. 37, no. 1, pp. 232–240, 2013.
[3] M. Etxeberria, C. Pacheco, J. M. Meneses, and I. Berridi, “Properties of concrete using metallurgical industrial by-products as aggregates,” Construction and Building Materials, vol. 24, no. 9, pp. 1594–1600, 2010.
[4] Y. Pontikes, P. T. Jones, D. Geysen, and B. Blanpain, “Options to prevent dicalcium silicate-driven disintegration of stainless steel slags,” Archives of Metallurgy and Materials, vol. 55, no. 4, pp. 1167–1172, 2010.
[5] M. A. Mikheenkov, O. Y. Sheshukov, I. V. Nekrasov, D. K. Egiazar’yan, and D. A. Lobanov, “Production of mineral binder from steel-smelting slag,” Steel in Translation, vol. 46, no. 3, pp. 232–235, 2016.