Utilization of Solid Waste Pulp Green Liquor Dregs and Slaker Grits for Rooftile Production Application
Abstract
This study aims to utilize solid waste pulp green liquor dregs and slaker grits by analyzing the effect of adding solid waste green liquor dregs and slaker grits on water absorption and tile compressive strength, analyzing the chemical content of solid waste green liquor pulp dregs and slaker grits and concrete tile products and chemical morphology of the samples. The method used in this research is pressing. The results of the water absorption test for concrete roof tiles with the addition of 0%, 5%, 10%, and 15% solid waste green liquor pulp and slaker grits were 8.4%, 6.4%, 7.5%, and 9.4%. Testing the compressive strength of concrete tiles with the addition of 0%, 5%, 10%, and 15% solid waste green liquor pulp and slaker grits was 19.0 MPa, 19.7 MPa, 18.6 MPa, and 18.3 MPa. The chemical content of solid waste pulp before and after the finished concrete tile product is in accordance with the building blocks of the tile which consists of compounds Al2O3, SiO2, Fe2O3, and CaO. From the above test, it can be concluded that the addition of solid waste pulp can produce quality concrete roof tiles with reference to the value of SNI 0096-2007, that the maximum water absorption value of tile is 10% and the compressive strength of roof tiles is at least 6.0 MPa.
Keywords: solid waste, green liquor, slaker grits, rooftile
References
[1] M.W. Anggreni, “Pengolahan limbah padat sebagai bagian penerapam konsep green building,” (2012).
[2] Simão L, Hotza D, Raupp-Pereira F, Labrincha JA, Montedo OR. Wastes from pulp and paper mills - a review of generation and recycling alternatives. Ceramica. 2018;64(371):443–53.
[3] Ribeiro dos Santos V, Dezena Cabrelon M, de Sousa Trichês E, Quinteiro E. Green liquor dregs and slaker grits residues characterization of a pulp and paper mill for future application on ceramic products. J Clean Prod. 2019;240:118220.
[4] Almeida HC, da Silveira CB, Ernani PR, Campos ML, Almeida D. Composição química de um resíduo alcalino da indústria de papel e celulose (dregs). Quim Nova. 2007;30(7):1669–72.
[5] F.B. Harefa, “Pemanfaatan limbah padat pulp grits dan dregs dengan penambahan kaolin sebagai bahan pembuatan keramik konstruksi,” (2009).
[6] Badan Standardisasi Nasional 0096:2007, Genteng beton. Jakarta, 2007.
[7] Azevedo AR, Vieira CM, Ferreira WM, Faria KC, Pedroti LG, Mendes BC. Potential use of ceramic waste as precursor in the geopolymerization reaction for the production of ceramic roof tiles. J Build Eng. 2020;29(9):101156.
[8] Haris and Suratnan. Studi eksperimental kuat tekan beton dengan menstubtitusikan limbah batu bata pada semen. Siimo Engineering: Journal Teknik Sipil. 2020;4(1):39– 52.
[9] Martínez-Lage I, Velay-Lizancos M, Vázquez-Burgo P, Rivas-Fernández M, Vázquez- Herrero C, Ramírez-Rodríguez A, et al. Concretes and mortars with waste paper industry: biomass ash and dregs. J Environ Manage. 2016 Oct;181(1):863–73.
[10] Bachtiar IM. Sudarsono, and A. Kadir, “Pengaruh fraksi volume pasir terhadap kekuatan bending, densitas dan porositas keramik berbahan basar tanah liat.,”. ETHALPHY: Jurnal Ilmiah Mahasiswa Teknik Mesin. 2019;4(9):100–4.