Autoclave Precipitation Of Iron From Zinc Sulfate Solutions
Abstract
Zinc concentrates processing technology that includes high-temperature roasting – leaching of cinder – purification of leached liquor – electrowinning is the most widely used technology. Purified solution, which is fed to the electrowinning stage, has a high sensitivity to such an impurity as iron. The presence of iron in the zinc electrolyte has a negative influence both on the current efficiency and the quality of the cathode zinc.
The application of autoclave equipment for iron removal from zinc sulfate solutions, obtained after the leaching stage of zinc cinder, is described in this article. All experiments were carried out with a model solution of following composition, g/L: 10-33 H2SO4, 1.5 Cu, 5 Mn, 110 Zn, 2.5 Fe. Neutralization and purification of the solution was implemented during low-temperature pressure leaching of the zinc cinder.
The optimum conditions for iron precipitation from zinc solution are following: molar flow rate Zn(cinder) / H2SO4 = 1.3, t = 80 °C, τ = 1 hour, PO2 = 0.2 MPa. It was found, that the concentration of iron can be reduced up to 1-2 mg/L, whereas 83.5% of Zn and 52.1% of Cu being recovered into the solution from zinc cinder.
References
[1] M. Sethurajan, D. Huguenot, R. Jain et al., “Leaching and selective zinc recovery from acidic leachates of zinc metallurgical leach residues,” Journal of Hazardous Materials, vol. 324, pp. 71–82, 2017.
[2] J. Han, W. Liu, W. Qin, Y. Zheng, and H. Luo, “Optimization Study on the Leaching of High Iron-Bearing Zinc Calcine After Reduction Roasting,” Metallurgical and Materials Transactions B: Process Metallurgy and Materials Processing Science, vol. 47, no. 1, pp. 686–693, 2016.
[3] R. Abelha, L. Lanza, C. R. Ara, and T. Matencio, “Effect of iron on zinc electrowinning usng sulfate solutions, Tecnol. Metal. Mater. Miner,” São Paulo, vol. 4, pp. 3583–3593, 2010.
[4] Z.-G. Ru, C.-X. Pan, G.-H. Liu, X.-T. Wang, G.-Y. Dou, and K.-S. Zhu, “Leaching and recovery of zinc from leaching residue of zinc calcine based on membrane filter press,” Transactions of Nonferrous Metals Society of China (English Edition), vol. 25, no. 2, pp. 622–627, 2015.
[5] J. Han, W. Liu, W. Qin, K. Yang, D. Wang, and H. Luo, “Innovative methodology for comprehensive utilization of high iron bearing zinc calcine,” Separation and Purification Technology, vol. 154, pp. 263–270, 2015.
[6] J. Han, W. Liu, W. Qin, B. Peng, K. Yang, and Y. Zheng, “Recovery of zinc and iron from high iron-bearing zinc calcine by selective reduction roasting,” Journal of Industrial and Engineering Chemistry, vol. 22, pp. 272–279, 2015.
[7] H. Han, W. Sun, Y. Hu, and H. Tang, “The application of zinc calcine as a neutralizing agent for the goethite process in zinc hydrometallurgy,” Hydrometallurgy, vol. 147- 148, pp. 120–126, 2014.
[8] C. Akilan and M. J. Nicol, “Kinetics of the oxidation of iron(II) by oxygen and hydrogen peroxide in concentrated chloride solutions – A re-evaluation and comparison with the oxidation of copper(I),” Hydrometallurgy, vol. 166, pp. 123– 129, 2016.
[9] E. R. Encina, M. Distaso, R. N. Klupp Taylor, and W. Peukert, “Synthesis of goethite α- FeOOH particles by air oxidation of ferrous hydroxide Fe(OH)2 suspensions: Insight on the formation mechanism,” Crystal Growth and Design, vol. 15, no. 1, pp. 194–203, 2015.